Model: H-70 WT
Application: Sheathing layer for various wire and cable
Color: White, other color is also available;
Packing: 25kg/bag
Temperature Degree: 70℃
Specification:
| 1. |
Appearance |
---- |
Good plasticizing,
Uniform color, no obvious impurity |
| 2. |
Values to be obtained for the tensile strength |
MPa |
≥15.0 |
| 3. |
Values to be obtained for the elongation at break |
% |
≥150 |
| 4. |
Ageing in air oven(100℃±2℃, 168h) |
|
|
| 4.1 |
Value to be obtained for the tensile strength after ageing: |
MPa |
≥15.0 |
| 4.2 |
Max variation for the tensile strength: |
% |
±20 |
| 4.3 |
Values to be obtained for the elongation at break after ageing |
% |
≥180 |
| 4.4 |
Max variation for the elongation at break |
% |
±20 |
| 5 |
Loss of mass after ageing (100℃±2℃, 168h) |
g/m2 |
≤23 |
| 6 |
Thermal deformation |
% |
≤50 |
| 7 |
Impact embrittlement performance |
Invalid value |
≤15/30 |
| 8 |
Thermal stability at 200℃ |
Min |
≥50 |
| 9 |
Volume resistivity at 20℃ |
Ω·m |
≥1.0x108 |
| 10 |
Dielectric Strength |
MV/m |
≥18 |
Test Standard: GB/T 8815-2008 Plasticized Polyvinyl Chloride (PVC) Compounds for Wire and Cable.
Rohs Compliant.